Projection Welding:

The projection welding process is similar to spot welding except that the welding pressure, and welding current. Hence the welding heat are localized by making projection or embossments on one or both of the work pieces to be joined. Such projections are made at all points where a weld spot is desired.

01-projection welding

The projections have a diameter on the face equal to about the thickness of the stock and extend about 60 percentage of the stock thickness above the stock.

Operation:

The welding current is passed through the joint, welding heat is generated at these projections. Under the welding pressure the projections flatten allowing the two surfaces to be joined to come together. The melted projection becomes the weld.

01-projection welding machine - resistance projection welding process

The number of projections made in a joint should permit proper contact between the work pieces at the projections. The ideal number is three as the two sheets will always be in contact at three points. The maximum number of projections that can be satisfactorily handled is about six.

Special attention must be paid to the selection of correct pressing force at the beginning of the welding process. Use of excessive force causes the projection to collapse before the weld pool is created, which increases the contact surface and reduces current density. Variation in tensile strength of the workpiece may make welding more difficult, because it may result in projections of different sizes, in addition to which they flatten in different ways during welding.

When welding several projections at the same time, problems may occur in the heat balance of the joint or in the flattening of the projections. Problems can often be avoided by increasing the distance between projections. The recommended distance is four times the diameter of the projection.

Welding soft materials may be difficult if the workpiece thickness is less than 0.50 mm, because projections may collapse before welding current is applied.

For a successful projection weld the projections made on the parts should have the following characteristics:

1. The projections should be stiff enough to take the squeeze force before the current is passed.

2. The projections should have sufficient mass to heat a spot in the plane surface to welding temperature

3. The projections should collapse during welding without splashing between the sheets being welded.

4. The projections should be properly formed without any partial shearing.

5. It should be possible to form the projections without disturbing the other portions of the component.

01-projection welding fixtures - projection welding gun

Advantages of Projection Welding:

1. More than one spot weld can be made in a single operation, so the operation is very fast.

2. Welding current and pressure required is less

3. It helps in obtaining a satisfactory heat balance in welding of difficult to weld combinations of metals and thickness.

4. Closer spacing of welds is possible

5. Electrodes can be shaped to act as assembly fixtures for mass welding of parts

6. Uniform welds with good finish are produced.

7. Suitable for automation

8. Filler metals are not used. Hence clean weld joints are obtained

Disadvantages of projection welding:

1. Projections cannot be made in thin work pieces.

2. Thin work pieces cannot withstand the electrode pressure

3. Additional operation is required after the welding process is over.

4. Equipment is costlier

Applications of projection welding:

01-projection welding nuts - projection welding electrodes

1. A very common use of projection welding is the use of special nuts that have projections on the portion of the part to be welded to the assembly. Also, used for welding parts of refrigerator, condensers, refrigerator racks & grills, bushings, studs, nuts, handles etc..

You might also like

Resistance Spot Welding | Resistance Spot Welding How It Works | Resistance Spot Welding Theory
Resistance Spot Welding: In spot welding the weld is effected by the heat produced due to resistance...

Resistance Welding Process | Pipe Welding Equipment | Resistance Welding Dissimilar Metals
Resistance Welding: Resistance welding is a process in which two or more parts are welded by the coordinated...

Resistance Seam Welding Process | What Is Resistance Seam Welding | Seam Welding Chassis
Resistance Seam Welding: In principle seam welding is similar to spot welding except that it uses disc...

Ultrasonic Welding Machine | Ultrasonic Plastic Welding | Ultrasonic Welding Basics
Ultrasonic Welding: Ultrasonic welding is represented as a friction welding method, where oxides and...

Tagged with:
preload preload preload